Özet:

In this study, the aim is to improve the surface properties against the inhibitor effects that the AISI 316 stainless steel is exposed during use using the atmospheric plasma spray cover method. The powder has two different chemical properties to be used to study the resistance to swelling. The two are mixed homogeneously. The powder mixture is made with 100% woka 7202 powder (Ni 78-82% Cr 18-22) and diamalloy 2002 (Ni 66%-Cr 18%) powder mixture. The covering process was carried out by taking optical image and SEM-EDS analysis from the cutting structures of the samples applied.  The XRD analysis was implemented and then hardness measurements were made. CSM is tested with the CSM test device. Measurements of surface smoothness have been taken with SEM-EDS analysis after swelling. The welding experiment was carried out in different speed, distance and load parameters using aluminum ball.

Anahtar Kelimeler:

Özet:

Bu çalışmada; AISI 316 paslanmaz çeliğinin kullanım sırasında maruz kaldığı aşındırıcı etkilere karşı yüzey özelliklerinin atmosferik plazma sprey kaplama yöntemi kullanılarak iyileştirilmesi amaçlanmıştır. Aşınma dayanımını inceleyebilmek için iki farklı kimyasal özelliğe sahip toz kullanılmıştır. Söz konusu bu iki toz homojen olarak karıştırılmıştır. Toz karışımı; %100 woka 7202 tozu (Ni 78-82% Cr 18-22) ve diamalloy 2002 (Ni 66%-Cr 18%) toz karışımı tercih edilerek kaplama yapılmıştır. Kaplama işlemi uygulanmış numunelerin kesit yapılarından optik görüntü ve SEM-EDS analizi alınarak mikroyapı incelemesi yapılmıştır.  XRD analizi uygulanıp sonrasında sertlik ölçümleri yapılmıştır. CSM Aşınma test cihazı ile aşınma testleri yapılmıştır. Aşınma sonrası SEM-EDS analizi ile yüzey pürüzlülüğü ölçümleri alınmıştır. Aşınma deneyi alümina bilya kullanılarak farklı hız, mesafe ve yük parametrelerinde gerçekleştirilmiştir.