A new, environmentally cleaner, technology of obtaining microcrystalline cellulose of fibers of hemp was proposed. The various stages of obtaining microcrystalline cellulose were studied and the optimum values of technological parameters of alkali extraction of hemp fibers, organosolv pulping, chelation and hydrolysis of cellulose were defined. It was determined that the consistent treatment of fibers of hemp by extraction of 5 % KOH solution during 210 minutes at the temperature of 95 °С, performic cooking in a mixture of 85 % formic acid and 30 % of hydrogen peroxide in the ratio of 60:40 of volume % at 100 °C during 210 min, chelation by the solution of trilon B of the concentration of 10 g/l during 30 min at 50 °C and hydrolysis by a mixture of 98 % acetic acid and 30 % of hydrogen peroxide solution in the ratio of 70:30 of volume %, allows obtaining microcrystalline cellulose in the form of white powder with a degree of polymerization 80 and the content of sulfate ash of 0.10 %. Using the methods of scanning electronic microscopy, thermogravimentric analysis and Xray diffraction confirmed that the consistent multistage chemical treatment increases the content of crystalline part of cellulose by the removal of extractive and mineral substances, hemicelllulose and amorphous fraction of cellulose of the fibers of hemp. Application of the proposed technology of obtaining microcrystalline cellulose from the fibers of hemp is environmentally more friendly and enables to reduce significantly the cost of finished products by using national, annually renewable plant raw materials compared to imported cotton or pine cellulose. Author Biographies Valerii Barbash, National Technical University Ukraine “Kyiv Polytechnic Institute” Peremohy ave., 37, Kyiv, Ukraine, 03056 PhD, Associate professor Department of ecology and plant polymer technologies
Alan : Fen Bilimleri ve Matematik
Dergi Türü : Uluslararası
Benzer Makaleler | Yazar | # |
---|
Makale | Yazar | # |
---|