Abstract:

The electrical discharge machining-process (EDM) is a smart solution to optimize the manufacturing chain of customized and complex shaped ceramic components. To comply with the high requirements for the machine and mold design, it is necessary to improve the mechanical properties of ED-machinable ceramics. In this study, ceramic composites with a tetragonal zirconia matrix and tungsten carbide as electrically conductive dispersion were investigated. To improve the toughness of this high strength material, co-stabilized zirconia coated with yttria and neodymia as dopants were used in the compositions with 1.5/1.5 and 1.75/1.25 mol %. These recipes were compared to commercial 3Y-TZP as a reference matrix material combined with the same WC raw powder. The electrically conductive phase content was varied from 20 to 28 vol %. For all compositions, the ceramic blanks were hot pressed at identical dwell and pressure, but with various sintering temperatures (1300 °C to 1450 °C) and then tested with respect to the mechanical and electrical properties. By variation of the stabilizer system, a significantly higher toughness of up to 11.3 MPa√m compared to 5.3 MPa√m for 3Y-TZP-20WC is achieved while the bending strength stays at a comparable high level of >1500 MPa.

Keywords: