Abstract:

This study aims to improve the corrosion properties of (AISI 1040) materials used in the automotive industry. For this purpose, two different coating techniques were applied to the same surface. As part of the research, different passivation processes (transparent, blue, yellow, and black) were applied to alkaline Zn-Ni coatings. Geomet 321 and Geomet ML Black coatings were deposited on the passivation layer to form a double-layer coating. In order to investigate the adhesion and corrosion effects of these coatings, a dry adhesion test, a water test, a humidity test, and a salt spray test were carried out, and cross-cut adhesion tests were carried out after each corrosion test. After all these tests, rust formation was analysed by visual analysis, and atomic weight percentages and coating thicknesses were examined by X-ray. The transparent passivation after the Zn-Ni coating fully satisfied both adhesion and corrosion protection requirements for 321 and ML Black coatings. No red rust formation was observed on the coating samples after the test; only partial white rust formation was observed, and no peeling of the coating layer was detected in the adhesion tests. As a result, the optimum result of the passivation processes used for Geomet 321+ML Black coatings applied after the Zn-Ni + passivation process was obtained with transparent passivated Zn-Ni coatings. Even after 1200 hours, no red rust was observed in passivated Zn-Ni coating+ Geomet 321+ Geomet ML Black.

Keywords: