Özet:

In this study, the possibilities of production of gabro-based glass and glass-ceramic materials were studied. For this purpose, two different compounds were prepared by participating in the gabroya MgO, Al2O3, B2O3 and P2O5, prepared these compounds were erguited at 1500 °C and gabro-based glasses were obtained. Glass-ceramic conversions have been carried out on these glasses by applying 2 different heat processing programs, 3 hours at 1000 °C and 3 hours at 1000 °C + 1100 °C 3 hours. Phase structures of glass and glass-ceramic materials have been studied with X-ray diffraction (XRD). There are also measurements of the hardness and braking density of the glass and glass-ceramic materials. Characteristics made with XRD and erguiting after gabro-based materials have been determined that the cams are in amorphic structure. After the heating processes, the glass-ceramic conversion occurred, the crystal phases were broken into the glass matrice, and increases in hardness and breakdown density were also detected.